Molybdenum Plates For High Temperature Furnace Components
1. Description of Molybdenum Plate For High Temperature Furnace Components:
Molybdenum plate is an important product, which is made of molybdenum material. Molybdenum products with a thickness of 0.2~20mm are called molybdenum plates. Molybdenum plate is widely used in the production of high temperature furnace parts and electronic component materials.
2. Size of Molybdenum Plate For High Temperature Furnace Components:
Molybdenum plate
thickness:0.2mm-20mm wideth:10-700mm length:<2500mm
Purity:99.95%,99.97%
Grade:Mo-1,TZM,Mo-La,361,364
Standard:ASTM B386
Surface:black,polished,Alkaline washing,sandblasting
3. Main Chemical Composition of Molybdenum Plate For High Temperature Furnace Components:
Chemical content as per ASTM B386:
| Element | Composition % |
| Grade |
| 361(Mo-1) | 364(TZM) | 366(Mo-30%W) |
| C | 0.01 max. | 0.01~0.04 | 0.03 max. |
| O,max. | 0.007 | 0.03 | 0.0025 |
| N,max. | 0.002 | 0.002 | 0.002 |
| Fe, max. | 0.01 | 0.01 | 0.01 |
| Ni, max. | 0.005 | 0.005 | 0.005 |
| Si, max. | 0.01 | 0.005 | 0.01 |
| Ti | 0.4~0.55 | | |
| W | | | 27~33 |
| Zr | | 0.06~0.12 | |
| Mo | Remain | Remain | Remain |
4. Mechanical Character of Molybdenum Plate For High Temperature Furnace Components:
Performance requirements as per ASTM B386:
| Material type | Condition | Thickness inches(mm) | Tensile Strength B Min, klb/in2 (MPa) | Yield Strength 0.2% Residual Deformation, Min, klb/in2 (mm) | Elongation, min, % (2 inches or 50 mm) | Minimum bending radius |
| 361 | SR | ≤0.001(0.025) | 115(795) | 95(655) | 1 | |
| 364 | SR | 0.01~0.025(0.25~0.635) | 120(830) | 100(690) | 6 | 2t |
| ≥0.025~0.06(0.635~1.5) | 120(830) | 100(690) | 7 | 2t |
| ≥0.06~0.09(1.5~2.3) | 100(690) | 100(690) | 9 | |
| ≥0.09~0.189(2.3~4.75) | 120(830) | 100(690) | 10 | |
| 3/16~1/2(4.75~12.7) | 120(830) | 100(690) | 10 | |
| ≥1/2~1(12.7~25.4) | 110(760) | 95(655) | 10 | |
| ≥1~1-1/2(25.4~38) | 100(690) | 85(585) | 8 | |
| 364 | RX | ≥3/16~1-1/2(4.75~38) | 75(515) | 45(310) | 10 | |
| A SR=stress relief； RX=almost completely recrystallized , B Longitudinal and transverse testing between 65°F and 85°F (18°C and 29°C) C t=Material thickness D is limited by transverse rolling, transverse elongation is easy to edge. |
5. Thickness Tolerance of Molybdenum Plate For High Temperature Furnace Components:
As per ASTM B386 standard
| Width inch (mm) | Thickness, inch (mm) | Thickness, inch (mm) |
| ≤12(305) | ≥0.005~0.01(0.13~0.25) | ±0.001(±0.0254) |
| ≥0.01~0.02(0.25~0.51) | ±0.002(±0.0508) |
| ≥0.02(0.51) | ±10% |
| ≥12~24(305~610) | ≥0.01~0.025(0.25~0.64) | ±0.0025(±0.0635) |
| ≥0.025(0.64) | ±10% |
| ≥24~30(610~762) | ≥0.016~0.030(0.41~0.76) | ±0.003(±0.0762) |
| ≥0.03(0.76) | ±10% |
| ≥30~48 (762~1219) | ≥0.04(1.02) | ±10% |
| ≥0.1875(4.762) | ±10% |